Raw Material: | Synthetic Rubber |
---|---|
Material: | Styrene Butadiene Rubber |
Specification: | 35KG/bag |
Trademark: | KunLun |
Origin: | China |
Samples: |
---|
Suppliers with verified business licenses
TIANJIN SANZHI PETRO-CHEMICAL CO., LTD. | |||
SBR 1712 | |||
Items | Quality index | Method | |
Appearance | Non-polluting light-colored lump rubber without impurities | Visual measurement | |
Volatiles,%(mass fraction)≤ |
0.6 | GB/T 24131-2009 Hot roll method | |
Aah,%≤ |
0.5 | GB/T4498-1997 Method A | |
Organic acids, %(mass fraction) |
3.90-5.70 | GB/T8657-2000 Method A | |
Organic soaps, %(mass fraction) |
0.5 | GB/T8657-2000 Method A | |
Bound styrene, %(mass fraction) |
22.5-24.5 | GB/T 8658-1998 | |
Massed mooney viscosity,ML(1+4)100°C |
44-54 | GB/T1232. 1-2000 Roller method | |
Compound rubber Mooney viscosity, ML(1+4)100°C≤ |
70 | GB/T 8656-1998 Metohod A ASTM IRB No7carbon black ,GB/T1232. 1-2000 |
|
300% Modulus(145°C),MPa (Type I specimen, speed of 500mm/min) |
25min | 9.8-13.8 | GB/T8656-1998GB/T528-1998 Method A ASTM IRB No 7 carbon black, GB528-2009 Type I cutter |
35min | 12.1-16.1 | GB/T8656-1998GB/T528-1998 Method A ASTM IRB No 7 carbon black, GB528-2009 Type I cutter |
|
50min | 13.0-17.0 | GB/T8656-1998GB/T528-1998 Method A ASTM IRB No 7 carbon black, GB528-2009 Type I cutter |
|
Tensile strength (145°C,35min),MPa≥ (Type I specimen, speed of 500mm/min) |
19.4 | GB/T8656-1998GB/T528-1998 Method A ASTM IRB No 7 carbon black, GB528-2009 Type I cutter |
|
Elongation(145°C,35min),%≥ (Type I specimen, speed of 500mm/min) |
380 | GB/T8656-1998GB/T528-1998 Method A ASTM IRB No 7 carbon black, GB528-2009 Type I cutter |
|
Oil content, %(mass fraction) |
25.3-29.3 | SH/T 1718-2002 |