Styrene Butadiene Rubber, SBR 1502E, Soles manufacturer / supplier in China, offering SBR 1502E (Emulsion Type Styrene Butadiene Rubber), Acrylonitrile-Butadiene-Styrene Resin/Copolymer ABS 750A, ABS 0215A (Acrylonitrile-Butadiene-Styrene Resin/Copolymer) and so on.

Gold Member Since 2019
Audited Supplier
Supplier Homepage Products ESBR SBR 1502E (Emulsion Type Styrene Butadiene Rubber)

SBR 1502E (Emulsion Type Styrene Butadiene Rubber)

Get Latest Price
Min. Order / Reference FOB Price
19,985 kg US $1.57-2.93/ kg
Port: Tianjin, China
Payment Terms: L/C, T/T, D/P, Western Union, Paypal, Money Gram
Raw Material: Synthetic Rubber
Material: Styrene Butadiene Rubber
Specification: 35KG/bag
Trademark: KunLun
Origin: China

You Might Also Like

Loading...

Basic Info

Model NO.
SBR 1502E

Overview:
The product is produced using the low-temperature emulsion polymerization method with butadiene and styrene as monomers and the complex soap of potassium dispro?portionated rosinate or potassium rosinate soap with fatty acid soap as the emulsifier. It is free from nitrosamines and salt.

APPLICATIONS:
Environment friendly styrene-butadiene rubber (SBR), which has a wide application in producing color or light colored rubber products, such as soles, rubberized fabric, medical supplies, rubber rolls, tires and the rubber products which has an environ?mental requirement to raw rubber materials.
 
TIANJIN SANZHI PETRO-CHEMICAL CO., LTD.
SBR 1502E
ItemsQuality indexMethod
AppearanceNon-polluting light-colored lump rubber without impuritiesVisual measurement

Volatiles,%(mass fraction)≤
0.45GB/T 24131-2009 Hot roll method

Aah,%≤
0.5GB/T4498-1997 Method A

Organic acids, %(mass fraction)
4.50-6.75GB/T8657-2000 Method A

Organic soaps, %(mass fraction)
0.5GB/T8657-2000 Method A

Bound styrene, %(mass fraction)
22.5-24.5GB/T 8658-1998

 Massed mooney viscosity,ML(1+4)100°C
46-54GB/T1232. 1-2000 Roller method

Compound rubber Mooney viscosity, ML(1+4)100°C≤
93GB/T 8656-1998 Metohod A ASTM IRB
No7carbon black ,GB/T1232. 1-2000

300% Modulus(145°C),MPa
(Type I specimen,
 speed of 500mm/min)
25min13.6-17.6GB/T8656-1998GB/T528-1998 Method A ASTM IRB
No 7 carbon black, GB528-2009 Type I cutter
35min18.6-22.6GB/T8656-1998GB/T528-1998 Method A ASTM IRB
No 7 carbon black, GB528-2009 Type I cutter
50min19.5-23.5GB/T8656-1998GB/T528-1998 Method A ASTM IRB
No 7 carbon black, GB528-2009 Type I cutter

Tensile strength (145°C,35min),MPa≥
(Type I specimen,
speed of 500mm/min)
25.5GB/T8656-1998GB/T528-1998 Method A ASTM IRB
No 7 carbon black, GB528-2009 Type I cutter

Elongation(145°C,35min),%≥
(Type I specimen,
speed of 500mm/min)
340GB/T8656-1998GB/T528-1998 Method A ASTM IRB
No 7 carbon black, GB528-2009 Type I cutter

N-nitrosamines, %(mass fraction)
Not detectedQ/SY 1389-2011

 

Send your message to this supplier

*From:
*To:
avatar Miss luo
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Loading...

Contact Supplier

Miss luo